Has anyone ever experienced this phenomenon?
A part appears to be free of defects prior to peening, then after peening a scratch or nick becomes visible?
|
|
|
|
|
Joined: Feb 2006
Posts: 110
Member
|
|
Member
Joined: Feb 2006
Posts: 110 |
There appears to be two alternatives as to scratch origin. Either the scratch was present before peening or it was imposed after peening. If it was present before peening then the scratch cannot be sharp and must have appear to have been 'blurred' by the action of peening. If the scratch appears to be sharp, then it must have occurred after peening - as a result of part handling. A blurred scratch is rare but can be the result of a scratch having been smoothed over by a burnishing type of process applied prior to peening. During burnishing metal flows over the scratch hiding it from view. Subsequent peening then stretches the surface revealing a (blurred) scratch.
|
|
|
|
|
Joined: Mar 2010
Posts: 5
Member
|
|
Member
Joined: Mar 2010
Posts: 5 |
Could it be that something has gotten into the working mix of shot that is being cycled through and shot at the part causing damage when it hits? Maybe bit of metal or something? This would be applicable on a system without classifier screens to take out stuff like that, of course.
|
|
|
|
|
Joined: May 1999
Posts: 199
Member
|
|
OP
Member
Joined: May 1999
Posts: 199 |
The damage looks like a long scatch or goove thats been peened over. Problem is we are 100% sure it was not visible to the naked eye prior to peening. Socrates answer seems to have hit the nail on the head.
Thanks for the info.
|
|
|
|
|
Joined: Jul 2023
Posts: 5
Member
|
|
Member
Joined: Jul 2023
Posts: 5 |
Dear Sir,
With this scratch, How did you remove it? And after removed it, did you re-peen again?
Best regards,
David
|
|
|
|
|
|
|