Dear all,

We are a aerospace components manufacturer in china.

Recently we buy 2 tons cast steel shots form US, the shots meet to specification AMS-2431/1.
Opened the bag, we find that there have rust on the shots surface.
Could anybody tell me how to remove these rust, and no effect to shots quality. ?

In the para.3.6 of AMS-2431/1, Contamination shot shall be clean and free of dirt, grit, oil, or grease. means the clean is allowed for contamination shots.

And the rust will effect lower peening intensity and deficient peening coverage, or not ? or other peening quality, such as part colouration ?

Thank you very much.

Kevin

Joined: May 1999
Posts: 197
Member
Online Content
Member
Joined: May 1999
Posts: 197
You should load the shot into your machine and blast a hardend steel plate for as many cycles as it takes to remove the "rust".

Joined: Jul 2023
Posts: 5
D
Member
Offline
Member
D
Joined: Jul 2023
Posts: 5
Hi Kevin,
Did you have effectively action?


Best regards,
David
Joined: Jul 2015
Posts: 2
K
Member
Offline
Member
K
Joined: Jul 2015
Posts: 2
Kevin, this occurs quite commonly, especially when product is shipped overseas with freight sitting in containers over extended periods of time. At Ervin, we poly line all shipments, but rust is inevitable. As Walter mentioned above, it's best to cycle the media by blasting it against a target. Depending on the size of your machine and the quantity of shot it holds, you'll have to time it accordingly. Contact me if you need more details on how long this needs to be done for.

Rust is a surface phenomenon, and descaling it will not impact your arc height values. If the particle size gets reduced by impacts (which is the natural failure mode for any peening media), it will get eliminated by your airwash separator, cyclone or bottom screen in your classifier. 'Descaled' shot will also help with avoiding part discoloration.

For your information, AMS grade material goes through a conditioning process prior to shipment. In other words, there is no surface rust on the shot particle during shipment. Transit rust is what you're noticing on the product. We have a bulletin for proper shot storage as well that I am happy to email you if you wish.

We discussed this at a recent SAE meeting and none of us felt the need to make a statement about rust in the documents since it's subjective and a rather simple fix.

Hope this helps.