Reduction of impingement angle may reduce the peening coverage time but this might be a dangerous approach. The impact site may cause significant surface distortion leading to fracture nucleation.
Generally you would increase the media flow rate to reduce the coverage time. There are limits to this approach also.
Are you using air blast or wheel blast equipment? I need to know this to offer additional comments.