Definitely do not use this cross contaminated mix. Although the size is close, the density of the materials is not the same. This difference would affect your intensity / saturation curve. Not to mention the surface of the part may appear different than normal.
You may have some luck by running the material through a spiral separator.
http://profile-ind.com/ If not, I’m afraid it’s a lost cause.