Hard shot has less residual ductility than has softer shot. This means that there is a greater chance of particle fracture in use. Fracture would tend to occur more frequently when shot impacts hard items - such as test blocks - than when impacting soft aluminum alloy parts. Problems arise because fractured hard shot particles have enough kinetic energy to indent soft alloys severely - more severely than when impacting hard parts.