Shot Peening Overview

Author:  Jack Champaigne
Source:  Electronics Inc, The Shot Peener
Doc ID:  2001012
Year of Publication:  2001
Shot peening is a cold working process in which the surface of a part is bombarded with small spherical media called shot. Each piece of shot striking the material acts as a tiny peening hammer, imparting to the surface a small indentation or dimple. In order for the dimple to be created, the surface fibers of the material must be yielded in tension. Below the surface, the fibers try to restore the surface to its original shape, thereby producing below the dimple, a hemisphere of cold-worked material highly stressed in compression. Overlapping dimples develop an even layer of metal in residual compressive stress. It is well known that cracks will not initiate or propagate in a compressively stressed zone. Since nearly all fatigue and stress corrosion failures originate at the surface of a part, compressive stresses induced by shot peening provide considerable increases in part life. The maximum compressive residual stress produced at or under the surface of a part by shot peening is at least as great as half the yield strength of the material being peened.Many materials will also increase in surface hardness due to the coldworking effect of shot peening. Benefits obtained by shot peening are the result of the effect of the compressive stress and the cold working induced. Compressive stresses are beneficial in increasing resistance to fatigue failures, corrosion fatigue, stress by corrosion cracking, hydrogen assisted cracking, fretting, galling and erosion caused by cavitation. Benefits obtained due to cold working include work hardening, intergranular corrosion resistance, surface texturing, closing of porosity and testing the bond of coatings. Both compressive stresses and cold-worked effects are used in the application of shot peening in forming metal parts.

Download PDF